Copper Alloys - Mechanical Properties - Extract from EN 1652
Previous Page
Print Page
| Material Designation EN 1652 or (Alloy..) |
Nearest Fit | Material Condition |
U.T.S. Rm N/mm2 |
0.2% Proof Stress N/mm2 |
Elongation A50 % min |
Hardness VPN |
||
|---|---|---|---|---|---|---|---|---|
| Symbol | Number | UNS | BS 2870 | |||||
| Brasses | ||||||||
| CuZn30 | CW505L | C26000 | CZ106 | R270 H055 |
270 - 350 | 160 max | 40 | - |
| - | - | - | 55 - 90 | |||||
| R350 H095 |
350 - 430 | 170 min | 21 | - | ||||
| - | - | - | 95 - 125 | |||||
| R410 H120 |
410 - 490 | 260 min | 9 | - | ||||
| - | - | - | 120 - 155 | |||||
| R480 H150 |
480 min | 430 min | - | - | ||||
| - | - | - | 150 min | |||||
| CuZn33 | CW506L | C26800 | CZ107 | R280 H055 |
280 - 380 | 170 max | 50 | - |
| - | - | - | 55 - 90 | |||||
| R350 H095 |
350 - 430 | 170 min | 23 | - | ||||
| - | - | - | 95 - 125 | |||||
| R420 H125 |
420 - 500 | 300 min | 6 | - | ||||
| - | - | - | 125 - 155 | |||||
| R500 H155 |
500 min | 450 min | - | - | ||||
| - | - | - | 155 min | |||||
| CuZn37 | CW508L | C27200 | CZ108 | R300 H055 |
300 - 370 | 180 max | 38 | - |
| - | - | - | 55 - 95 | |||||
| R350 H095 |
350 - 400 | 170 min | 19 | - | ||||
| - | - | - | 95 - 125 | |||||
| R410 H120 |
410 - 490 | 300 min | 8 | - | ||||
| - | - | - | 120 - 155 | |||||
| R480 H150 |
480 - 560 | 430 min | 3 | - | ||||
| - | - | - | 150 - 180 | |||||
| R550 H170 |
550 min | 500 min | - | - | ||||
| - | - | - | 170 min | |||||
| Phosphor Bronzes | ||||||||
| CuSn5 | CW451K | C51000 | PB102 | R310 H075 |
310 - 390 | 250 max | 45 | - |
| - | - | - | 75 - 105 | |||||
| R400 H120 |
400 - 500 | 240 min | 14 | - | ||||
| - | - | - | 120 - 160 | |||||
| R490 H160 |
490 - 580 | 430 min | 8 | - | ||||
| - | - | - | 160 - 190 | |||||
| R550 H180 |
550 - 640 | 510 min | 4 | - | ||||
| - | - | - | 180 - 210 | |||||
| R630 H200 |
630 - 720 | 600 min | 2 | - | ||||
| - | - | - | 200 - 230 | |||||
| R690 H220 |
690 min | 670 min | - | - | ||||
| - | - | - | 220 min | |||||
| CuSn6 | CW452K | C51900 | PB103 | R350 H080 |
350 - 420 | 300 max | 45 | - |
| - | - | - | 80 - 110 | |||||
| R420 H125 |
420 - 520 | 260 min | 17 | - | ||||
| - | - | - | 125 - 165 | |||||
| R500 H160 |
500 - 590 | 450 min | 8 | - | ||||
| - | - | - | 160 - 190 | |||||
| R560 H180 |
560 - 650 | 500 min | 5 | - | ||||
| - | - | - | 180 - 210 | |||||
| R640 H200 |
640 - 730 | 600 min | 3 | - | ||||
| - | - | - | 200 - 230 | |||||
| R720 H220 |
720 min | 690 min | - | - | ||||
| - | - | - | 220 min | |||||
| Material Designation EN 1652 or (Alloy..) |
Nearest Fit | Material Condition |
U.T.S. Rm N/mm2 |
0.2% Proof Stress N/mm2 |
Elongation A50 % min |
Hardness VPN |
||
| Symbol | Number | UNS | BS 2870 | |||||
| Nickel Silvers | ||||||||
| CuNi10Zn27 CuNi12Zn24 | CW401J CW403J | C74500 C75700 | NS103 NS104 | R360 H080 |
360 - 430 | 230 max | 35 | - |
| - | - | - | 80 - 110 | |||||
| R430 H110 |
430 - 510 | 230 min | 8 | - | ||||
| - | - | - | 110 - 150 | |||||
| R490 H150 |
490 - 580 | 400 min | - | - | ||||
| - | - | - | 150 - 180 | |||||
| R550 H170 |
550 - 640 | 480 min | - | - | ||||
| - | - | - | 170 - 200 | |||||
| R620 H190 |
620 min | 580 min | - | - | ||||
| - | - | - | 190 min | |||||
| CuNi18Zn20 | CW409J | C75200 | NS106 | R380 H085 |
380 - 450 | 250 max | 27 | - |
| - | - | - | 85 - 115 | |||||
| R450 H115 |
450 - 520 | 250 min | 9 | - | ||||
| - | - | - | 115 - 160 | |||||
| R500 H160 |
500 - 590 | 410 min | 3 | - | ||||
| - | - | - | 160 - 190 | |||||
| R580 H180 |
580 - 670 | 510 min | - | - | ||||
| - | - | - | 180 - 210 | |||||
| R640 H200 |
640 - 730 | 600 min | - | - | ||||
| - | - | - | 200 - 230 | |||||
| CuNi18Zn27 | CW410J | C77000 | NS107 | R390 H090 |
390 - 470 | 280 max | 30 | - |
| - | - | - | 90 - 120 | |||||
| R470 H120 |
470 - 540 | 280 min | 11 | - | ||||
| - | - | - | 120 - 170 | |||||
| R540 H170 |
540 - 630 | 450 min | 3 | - | ||||
| - | - | - | 170 - 200 | |||||
| R600 H190 |
600 - 700 | 550 min | - | - | ||||
| - | - | - | 190 - 220 | |||||
| R700 H220 |
700 - 800 | 660 min | - | - | ||||
| - | - | - | 220 - 250 | |||||
| Other Alloys | ||||||||
| CuNi9Sn2 (Alloy 725) | CW351H | C72500 | - | R340 H070 |
340 - 410 | 250 max | 30 | - |
| - | - | - | 70 - 100 | |||||
| R380 H110 |
380 - 470 | 200 min | 8 | - | ||||
| - | - | - | 110 - 150 | |||||
| R450 H140 |
450 - 530 | 370 min | 4 | - | ||||
| - | - | - | 140 - 170 | |||||
| R500 H160 |
500 - 580 | 450 min | 2 | - | ||||
| - | - | - | 160 - 190 | |||||
| R560 H180 |
560 - 650 | 520 min | - | - | ||||
| - | - | - | 180 - 210 | |||||
| (Alloy 194) | - | C19400 | - | Annealed | 300 min | - | 25 | 85 max |
| Half hard | 360 min | - | 15 | 100 - 130 | ||||
| Hard | 410 min | - | 5 | 130 - 140 | ||||
| Extra hard | 460 min | - | 2 | 140 min | ||||